3D printed thermoplastic healing agent (blue overlay) on glass-fiber reinforcement (left); infrared thermograph during in situ self-healing of a fractured fiber-composite (middle); 3D printed healing agent (blue) on carbon-fiber reinforcement (right).
Image Credit: Jason Patrick, NC State University.
Scientific Frontline: "At a Glance" Summary
- Main Discovery: Researchers developed a self-healing fiber-reinforced polymer (FRP) composite capable of enduring more than 1,000 autonomous repair cycles, offering a potential solution to the persistent problem of delamination.
- Mechanism: The system utilizes a thermoplastic healing agent (poly(ethylene-co-methacrylic acid)) 3D-printed onto fiber reinforcements, which is activated by embedded carbon-based heater layers to melt and re-bond cracks.
- Key Data: Experimental testing verified 1,000 fracture-and-heal cycles, with fracture resistance starting at 175% of standard non-healing composites and maintaining approximately 60% strength after extensive cycling.
- Context: Predictive modeling estimates the material could last 125 years with quarterly healing or up to 500 years with annual healing, vastly exceeding the typical 15–40 year lifespan of current FRPs.
- Significance: This technology is positioned to drastically reduce maintenance costs and waste in aerospace and renewable energy sectors, particularly for spacecraft and wind turbines where manual repair is difficult or impossible.
- Critical Detail: The gradual decline in healing efficacy is attributed to the accumulation of brittle fiber micro-debris and waning chemical reactions at the interface, though performance remains statistically viable for century-scale use.
Researchers have created a self-healing composite that is tougher than materials currently used in aircraft wings, turbine blades and other applications – and can repair itself more than 1,000 times. The researchers estimate their self-healing strategy can extend the lifetime of conventional fiber-reinforced composite materials by centuries compared to the current decades-long design-life.
“This would significantly drive down costs and labor associated with replacing damaged composite components, and reduce the amount of energy consumed and waste produced by many industrial sectors – because they’ll have fewer broken parts to manually inspect, repair or throw away,” says Jason Patrick, corresponding author of the paper and an associate professor of civil, construction and environmental engineering at North Carolina State University.
At issue are fiber-reinforced polymer (FRP) composites, which are valued for their high strength-to-weight ratio and are commonly used in aircraft, automobiles, wind-turbines, spacecraft and other modern structural applications. FRP composites consist of layers of fibers, such as glass or carbon fiber, that are bonded together by a polymer matrix, often epoxy. The self-healing technique developed by the NC State researchers targets interlaminar delamination, which occurs when cracks within the composite form and cause the fiber layers to separate from the matrix.
“Delamination has been a challenge for FRP composites since the 1930s,” Patrick says. “We believe the self-healing technology that we’ve developed could be a long-term solution for delamination, allowing components to last for centuries. That’s far beyond the typical lifespan of conventional FRP composites, which ranges from 15-40 years.”
The self-healing material resembles conventional FRP composites, but with two additional features. First, the researchers 3D-print a thermoplastic healing agent onto the fiber reinforcement, creating a polymer-patterned interlayer that makes the laminate two to four times more resistant to delamination. Second, the researchers embed thin, carbon-based heater layers into the material that warm up when an electrical current is applied. The heat melts the healing agent, which then flows into cracks and microfractures and re-bonds delaminated interfaces – restoring structural performance.
To evaluate long-term healing performance, the team built an automated testing system that repeatedly applied tensile force to an FRP composite producing a 50 millimeter-long delamination, then triggered thermal remending. The experimental setup ran 1,000 fracture-and-heal cycles continuously over 40 days, measuring resistance to delamination after each repair. In other words, the researchers cracked the material in the exact same way, healed it, and then measured how much load the material could handle before delaminating again. And they did that 1,000 times, an order-of-magnitude beyond their prior record.
“We found the fracture resistance of the self-healing material starts out well above unmodified composites,” says Jack Turicek, lead author of the paper and a graduate student at NC State. “Because our composite starts off significantly tougher than conventional composites, this self-healing material resists cracking better than the laminated composites currently out there for at least 500 cycles. And while its interlaminar toughness does decline after repeated healing, it does so very slowly.”
In real-world scenarios, healing would only be triggered after the material is damaged by hail, bird strikes or other events, or during scheduled maintenance. The researchers estimate the material could last 125 years with quarterly healing or 500 years with annual healing.
“This provides obvious value for large-scale and expensive technologies such as aircraft and wind turbines,” Patrick says. “But it could be exceptionally important for technologies such as spacecraft, which operate in largely inaccessible environments that would be difficult or impossible to repair via conventional methods on-site.”
The study also shed light on why recovery slowly declines over time. With continued cycling, the brittle reinforcing fibers progressively fracture – creating micro-debris that limits rebonding sites. In addition, chemical reactions where the healing agent interfaces with the fibers and polymer matrix decline over time. Even so, modeling suggests the self-healing will remain viable over extremely long time scales.
“Despite the inherent chemo-physical mechanisms that slowly reduce healing efficacy, we have predicted that perpetual repair is possible through statistical modeling that is well suited for capturing such phenomena,” says Kalyana Nakshatrala, co-author of the paper and the Carl F. Gauss Professor of Civil and Environmental Engineering at the University of Houston.
Patrick has patented and licensed the technology through his startup company, Structeryx Inc.
“We’re excited to work with industry and government partners to explore how this self-healing approach could be incorporated into their technologies, which has been strategically designed to integrate with existing composite manufacturing processes,” Patrick says.
Funding: This work was done with support from the Strategic Environmental Research and Development Program (SERDP) through grant W912HQ21C0044 and from the National Science Foundation, under grant 2137100.
Published in journal: Proceedings of the National Academy of Sciences
Authors: Jack S. Turicek, Zachary J. Phillips, Kalyana B. Nakshatrala, and Jason F. Patrick
Source/Credit: North Carolina State University | Matt Shipman